| Abstract: |
| The samples cut from U75V 60 kg/m heavy rail are heated to 900 ℃ in resistance furnace and then put into air spraying channel to be cooled for 80 s, and change air pressure from 0.16 MPa to 0.33 MPa, and observe the effect of air pressure on hardened layer. The thickness and hardness of hardened layer increases with the increase of air pressure, and the thickness is more than 24 mm at the center and top fillets of rail head, and more than 15 mm at the blow fillets of rail head when air pressure is more than 0.26 MPa. During the tempering after heat treatment, tempering temperature of rail head is more than 570 ℃ when air pressure is separately 0.16 MPa, 0.20 MPa and 0.23 MPa, which is higher than finishing temperature of pearlite transformation at the cooling rate of 3 ℃/s according to CCT curve of U75V steel. When air pressure is separately 0.6,0.30 and 0.33 MPa, the tempering temperature is 529 ℃ lower than finishing temperature of pearlite transformation at the cooling rate of 3 ℃/s. Under this condition, pearlite transformation is finished totally, so in order to reduce air consumption and control the cost, proper air pressure for U75V 60 kg/m heavy rail heat treating should be 0.26 MPa; the cooling rate increases with the increase of air pressure, and the average cooling rate on the surface of rail head is more than 3.21 ℃/s when air pressure is more than 0.26 MPa, and the largest cooling rate occurs at the top fillets of rail head. |
| Key words: air pressure hardened layer heavy rail heat treatment |
| DOI：10.11916/j.issn.1005-9113.2013.01.010 |
| Clc Number:TG162.82 |
| Fund: |