LiNi0.4Co0.2Mn0.4O2与LiMn2O4共混正极材料电化学性能

doi:10.11918/j.issn.0367-6234.2016.08.027

首页 > 过刊浏览>2016年第48卷第8期 >161-165. DOI:10.11918/j.issn.0367-6234.2016.08.027

LiNi0.4Co0.2Mn0.4O2与LiMn2O4共混正极材料电化学性能
DOI:
                        10.11918/j.issn.0367-6234.2016.08.027
                    
CSTR:
                        
                    
作者:
                        
                        
                    
作者单位:(1.哈尔滨工业大学 化工与化学学院,哈尔滨150001; 2.哈尔滨工程大学 材料科学与化学工程学院, 哈尔滨150001; 3.超威电源有限公司,浙江 长兴313100)
作者简介:吕艳卓(1975—),女,副教授,博士后； 王振波(1973—),男,教授,博士生导师; 柯克(1973—),男,教授,博士生导师
通讯作者:王振波,wangzhb@hit.edu.cn
中图分类号:O646
基金项目:国家自然科学基金青年基金(21203040);中国博士后基金面上项目(2014M561357); 浙江省博士后科研项目择优资助资金(zj140288); 黑龙江省自然科学基金(B201201)

Electrochemical performances of the co-mixed LiNi_0.4Co_0.2Mn_0.4O2 and LiMn₂O₄ as the positive-electrode material of lithium ion battery

Author:

Affiliation:

(1.School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin 150001, China; 2.College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin 150001, China; 3.Chaowei Power Co., LTD, Changxing 313100, Zhejiang, China)

Fund Project:

摘要

图/表

访问统计

参考文献

相似文献

引证文献

资源附件

文章评论

摘要:

为开发具有优良循环性能和安全性能的大型锂离子电池的正极材料，将不同比例的LiNi_0.4Co_0.2Mn_0.4O₂和LiMn₂O₄材料进行共混，研究了LiNi_0.4Co_0.2Mn_0.4O₂和LiMn₂O₄共混以及共混比例(10∶0、8∶2、7∶3、6∶4、5∶5、0∶10)对锂离子电池的首次放电性能、循环性能和倍率性能以及交流阻抗和循环伏安曲线的影响，并采用扫描电镜对电极材料进行了表征.研究结果表明，共混比例会影响材料的电化学性能，8∶2，7∶3和6∶4配比的混合材料的体积比容量、循环性能和倍率性能要好于纯LiNi_0.4Co_0.2Mn_0.4O₂和LiMn₂O₄材料.其中，8∶2配比的材料性能最好.

Abstract:

In order to explore the positive material with excellent cycling ability and good safety, the effects of co-mixed ratios(10∶0、8∶2、7∶3、6∶4、5∶5、0∶10) of LiNi_0.4Co_0.2Mn_0.4O₂with LiMn₂O₄as the positive material of lithium ion battery on the first discharging properties, cycling abilities, rate capabilities, impedance spectroscopy and cyclic voltammetry were investigated. The co-mixed electrode materials were also characterized by SEM. The results indicated that the co-mixed ratio affected the electrochemical performances of the co-mixed materials. The materials with the ratios of 8∶2, 7∶3 and 6∶4 showed higher specific volumetric capacity, better cyclic and rate performances than that of LiNi_0.4Co_0.2Mn_0.4O₂and LiMn₂O₄ materials. The co-mixed material with the ratio of 8∶2 is the best.

参考文献

相似文献

引证文献

引用本文

吕艳卓,王霄鹤,刘建武,王振波,柯克. LiNi_0.4Co_0.2Mn_0.4O₂与LiMn₂O₄共混正极材料电化学性能[J].哈尔滨工业大学学报,2016,48(8):161. DOI:10.11918/j. issn.0367-6234.2016.08.027

复制

文章指标

点击次数:
下载次数:
HTML阅读次数:
引用次数:

历史

收稿日期:2015-10-27
最后修改日期:
录用日期:
在线发布日期: 2016-07-11
出版日期:

出版声明

期刊订阅

引用本文

相关视频

分享

文章指标

历史

文章二维码