| 引用本文: | 陈慧敏,王雅君,徐国跃,余慧娟,邵春明,胡晨.低红外发射率涂层的力学性能研究[J].材料科学与工艺,2010,18(6):873-877.DOI:10.11951/j.issn.1005-0299.20100628. |
| CHEN Hui-min,WANG Ya-jun,XU Guo-yue,YU Hui-juan,SHAO Chun-ming,HU Chen.Study on the mechanical properties of low infrared emissivity coatings[J].Materials Science and Technology,2010,18(6):873-877.DOI:10.11951/j.issn.1005-0299.20100628. |
|
| 摘要: |
| 以铝粉为主要填料,以环氧改性有机硅树脂为粘合剂,制备了发射率低至0.10的环氧有机硅低红外发射率涂层.研究了分散剂、滑石粉和固化温度对涂层力学性能的影响,并对其在涂料中的作用机理进行了探讨.结果表明,当滑石粉的质量加入量为2%、分散剂的加入量为2%、热处理温度为200°C时,制得的涂层能在保持低红外发射率的同时具有最佳的力学性能. |
| 关键词: 红外发射率 涂层 力学性能 铝粉 环氧改性有机硅 |
| DOI：10.11951/j.issn.1005-0299.20100628 |
| 分类号:TQ630.1 |
| 基金项目: |
|
| Study on the mechanical properties of low infrared emissivity coatings |
|
CHEN Hui-min, WANG Ya-jun, XU Guo-yue, YU Hui-juan, SHAO Chun-ming, HU Chen
|
|
College of Material Science and Technology,Nanjing University of Aeronautics & Astronautics, Nanjing 211100,China
|
| Abstract: |
| Low infrared emissivity coatings were prepared by epoxy-modified silicone and aluminum as adhesives and inorganic paint,of which the lowest emissivity value is 0.10 at the wavelength of 8~14 μm.The influence of the content of dispersant,talcum powder and curing temperature on the impact strength,flexility and adhesion of the coatings were systematically investigated.Moreover,the mechanism of the mechanical properties of coatings was studied.These results showed that the mechanical properties reached to the maximum value when the content of dispersant was 2 wt.%,the content of talcum powder was 2 wt.% and the curing temperature was 200 °C,and the coatings kept the low infrared emissivity. |
| Key words: infrared emissivity coating mechanical properties aluminum epoxy-modified silicone |