| CuZn37黄铜板料微塑性成形中的尺寸效应研究 |
|
李河宗1,2, 董湘怀1, 王倩1, 申昱1, DIEHL A3, HAGENAH H3, ENGEL U3, MERKLEIN M3
|
|
1.上海交通大学塑性成形工程系;2.河北工程大学机电学院;3.Chair of Manufacturing Technology,University of Erlangen Nuremberg
|
|
| 摘要: |
| 为研究金属微塑性成形特点,对厚度不同及粗细两种晶粒尺寸的黄铜箔试样进行了单向拉伸和微弯曲实验,并采用经典塑性理论和应变梯度理论对弯曲回弹角进行了预测.粗晶粒板料试样单向拉伸实验表明,CuZn37黄铜的硬化曲线存在一种明显的尺寸效应,即板料厚度越小,屈服强度越高.弯曲回弹实验结果也存在另一种明显的尺寸效应现象,即板料厚度越小,回弹角越大.对这两种尺寸效应产生的原因进行了分析,指出应变梯度硬化对微成形工艺过程有重要影响. |
| 关键词: CuZn37黄铜箔 微塑性成形 回弹角 尺寸效应 应变梯度 |
| DOI：10.11951/j.issn.1005-0299.20110404 |
| 分类号:TG386 |
| 基金项目:国家自然科学基金项目(508350025097517450821003);German Federal Ministry of Education and Research BMBF(CHN08-041) |
|
| Size effects of CuZn37 brass foil in microforming |
|
LI He-zong1,2, ONG Xiang-huai1, WANG Qian1, SHEN Yu1, DIEHL A3, HAGENAH H3, ENGEL U3, MERKLEIN M3
|
|
1.Dept.of Plasticity Technology,Shanghai Jiao Tong University,Shanghai 200030,China;2.Dept.of Mechanical and Electrical Engineering,Hebei University of Engineering,Handan 056038,China;3.Chair of Manufacturing Technology,University of Erlangen-Nuremberg,Erlangen 91058,Germany
|
| Abstract: |
| Uniaxial tensile tests and microbending experiments of brass foil specimens are performed to investigate size effects of metal foils in microforming process.The specimens are annealed at two different temperatures to obtain fine and coarse grain structure.In the paper,the springback angle in microbending process is predicted based on the classical plasticity theory and strain gradient theory.In uniaxial tensile tests,the increasing of material strength with decreasing foil thickness is observed,which indicates obvious presence of size effects for CuZn37 brass foils,especially for coarse grain specimens.In microbending experiments,obvious size-dependences of springback angle are observed,in which the springback angle of metal foils is increasing with foil thickness decreasing.The reasons for these size effects are discussed and the strain gradient hardening is important to microforming process. |
| Key words: CuZn37 brass foil microforming springback angle size effect strain gradient |
|
|
|
|