| 引用本文: | 马天慧,杨春晖,孙亮,徐超,陈玉峰.正交结构LiGaS2的合成及表征[J].材料科学与工艺,2012,20(3):121-126.DOI:10.11951/j.issn.1005-0299.20120324. |
| MA Tian-hui,YANG Chun-hui,SUN Liang,XU Chao,CHEN Yu-feng.Synthesis and characterization of orthorhombic LiGaS2[J].Materials Science and Technology,2012,20(3):121-126.DOI:10.11951/j.issn.1005-0299.20120324. |
|
| 摘要: |
| 为了获得高纯单相LiGaS2多晶原料，采用LiGa与S化合法合成LiGaS2，并与传统的单质直接合成法相对比.利用垂直长石英管作为反应器，采用X射线衍射和Raman光谱对其结构进行表征，同时利用差热–热重分析和紫外光谱对其热性能和光学性能进行研究.研究表明：采用LiGa与S化合法可以获得单相、均一的LiGaS2多晶材料；LiGaS2中的Li–S键平均力常数为Li-S=16.0 N/m，Ga–S键平均力常数为Ga-S=39.6 N/m；LiGaS2多晶料的熔点为1 020 ℃，温度低于1 100 ℃，样品很稳定，没有分解现象；白色样品、黄色样品和灰色样品的紫外吸收边分别为323，435和496 nm. |
| 关键词: 合成 正交结构 硫化镓锂 Raman光谱 |
| DOI：10.11951/j.issn.1005-0299.20120324 |
| 分类号:TQ171 |
| 基金项目:国家自然科学基金资助项目（50902027）;牡丹江师范学院青年学术骨干研究项目（G201002）；黑龙江省教育厅青年学术骨干项目（1252G061） |
|
| Synthesis and characterization of orthorhombic LiGaS2 |
|
MA Tian-hui1,2,3, YANG Chun-hui1, SUN Liang1, XU Chao1, CHEN Yu-feng1
|
|
1.College of Chemistry and Chemical Engineering,Mudanjiang Normal University,Mudanjiang 157012，China;2.School of Chemical Engineering and Technology,Harbin Institute of Technology,Harbin 150001,China;3.3.School of Physics and Electronic Engineering,Yibin University,Yibin 644000,China
|
| Abstract: |
| In order to obtain pure and high-quality LiGaS2 polycrystalline material,a novel synthesis method from LiGa and S was proposed and compared with the direct synthesis method from elements.The vertical long tube quartz reactors were applied as the bottom of this reactor being the high temperature zone and the top of this reactor being the low temperature zone.The structure was characterized by the X-ray powder diffraction(XRD)and Raman spectra.The thermal behavior and optical property of samples were also studied by the simultaneous differential scanning calorimetry/thermogravimetric(TG-DTA)and ultraviolet visible diffuse reflectance spectra(UV-vis).The results show that the pure and high-quality LiGaS2 polycrystalline material can be obtained from the combinational method of LiGa and S.The effective force constants Li–S and Ga–S for Li–S and Ga–S interactions are determined to be 16.0 N/m and 39.6 N/m,respectively.The melting point of LiGaS2 is 1 020 ℃ and this material is stable under 1 100 ℃.The ultraviolet absorption edges of white,yellow and grey samples are 323,435 nm and 496 nm,respectively. |
| Key words: synthesis orthorhombic lattice lithium-gallium sulfide raman spectra |