| 高强耐热镁合金大型锻件组织性能研究 |
|
张浩1,2 ,张绪虎2,杜志惠2,周晓建2,阴中炜2,王少华3,朱秉诚3
|
|
(1.中国运载火箭技术研究院,北京 100076;2.航天材料及工艺研究所,北京 100076;3.空间物理重点实验室,北京 100076)
|
|
| 摘要: |
| 为了满足航天飞行器对结构减重的迫切需求,推动变形镁合金在航天飞行器上的应用,采用力学性能测试及显微组织分析的方法对高强耐热镁合金工业级大型锻件进行了研究。研究结果表明:锻前固溶处理不能完全消除晶间稀土元素的偏析,这些稀土元素最终以Mg24Y5、Mg5Gd等相的形式保留下来,并呈现出颗粒形态；锻环力学性能的各向异性随着变形温度的提高而降低；低于250 ℃时,该合金的断口呈现出准解理和韧性撕裂的混合特征,随着温度的升高,韧性断裂的比重逐渐加大,当变形温度提高到300 ℃时,呈现出韧窝聚集形断裂特征。 |
| 关键词: 镁合金 锻造 时效处理 力学性能 显微组织 偏析 |
| DOI：10.11951/j.issn.1005-0299.20130511 |
| 分类号: |
| 基金项目:国防基础科研计划资助项目(A0320110003). |
|
| Microstructure and mechanical property of large-scale high-strength and heat-resistant magnesium alloy |
|
ZHANG Hao1,2,ZHANG Xu-hu2,DU Zhi-hui2,ZHOU Xiao-jian2,YIN Zhong-wei2,WANG Shao-hua3,ZHU Bing-cheng3
|
|
( 1. China Academy of Launch Vehicle Technology,Beijing 100076, China ;2.Aerospace Research Institute of Material & Processing Technology, Beijing 100076, China;3.Science and Technology onSpace Physics Laboratory,Beijing 100076,China)
|
| Abstract: |
| In order to meet the urgent needs of structural weight reduction of spacecraft and promote the applications of wrought magnesium alloys on spacecraft, mechanical property testing and microstructure analysis were applied to investigate the large-scale high-strength and heat-resistant magnesium alloy. The results show that the segregation of rare-earth can not be removed, which has been changed to the phases like Mg24Y5、Mg5Gd. The anisotropism of the forging ring is weakened and the specific weight of tough fracture is increased as the temperature is increased. The fracture model is tough fracture when the temperature is 300 ℃. |
| Key words: magnisum alloy forging aging treatment mechanical property microstructure segregation |