| 引用本文: | 杨模聪,孙中刚,马锐,孟强,陈洁.2060搅拌摩擦焊对接接头显微组织与析出相分析[J].材料科学与工艺,2014,22(5):119-123.DOI:10.11951/j.issn.1005-0299.20140521. |
| YANG Mocong,SUN Zhonggang,MA Rui,MENG Qiang,CHEN Jie.Analysis for microstructure and precipitation phase evolution of friction stir welding 2060 butt joint[J].Materials Science and Technology,2014,22(5):119-123.DOI:10.11951/j.issn.1005-0299.20140521. |
|
| 摘要: |
| 本文选用Al-Li-Cu-Mg系铝锂合金2060,开展搅拌摩擦焊对接接头显微组织与析出相演变规律研究.搅拌摩擦焊对接接头,呈现典型的母材、热影响区、热机影响区和焊核区四区分布特点.母材为双向板条组织,在α板条中有大量三角形AlCu2Mn化合物析出,但在其它相区,当受到热影响时,该相消失；热影响区组织粗大,热机影响区晶粒受到机械力作用,前进侧拉长,后退侧破碎；焊核区为等轴晶组织,出现了高温析出相AlxCuxMn,均布于整个焊核区域.接头显微硬度在母材区最高,热影响区最低,焊核区低于母材,稳定在115 HV. |
| 关键词: 铝锂合金 搅拌摩擦焊 显微组织 相 显微硬度 |
| DOI：10.11951/j.issn.1005-0299.20140521 |
| 分类号:TG456.9 |
| 基金项目: |
|
| Analysis for microstructure and precipitation phase evolution of friction stir welding 2060 butt joint |
|
YANG Mocong1, SUN Zhonggang1, MA Rui1, MENG Qiang2, CHEN Jie1
|
|
(1. Shanghai Aircraft Manufacturing Co., Ltd, Shanghai 200436 China;2. China FSW Center, Beijing 100024,China)
|
| Abstract: |
| The microstructure and precipitation phase evolution of friction stir welding butt joint of the Al-Li-Cu-Mg-based aluminum-lithium alloy 2060 were investigated. The cross section of friction stir welding butt joint could be divided into four distinctive regions: base metal zone, heat-affected zone, thermal mechanically affected zone and weld nugget zone. The microstructure of the base metal consisted of bidirectional slat, large numbers of triangular AlCu2Mn compound precipitated from α lath, which would disappear when subjected to heat action in other zones. The heat-affected zone showed coarse crystal particles, and grain morphology was changed under the action of mechanical force in the thermal mechanically affected zone, stretched at the advancing side and compressed at the retreating side. The weld nugget zone was equiaxed grain structure, the high temperature precipitated phase AlxCuxMn distributed throughout the joint region uniformly. The highest microhardness existed in the base metal zone, and the lowest value was located in the heat-affected zone, with the weld nugget zone steadying at 115 HV, a little lower than the base metal. |
| Key words: Al-Li alloy friction stir welding microstructure phase microhardness |