| 引用本文: | 钟喜春,胡庚,郭兴家,刘仲武.粘结剂对粘结钕铁硼/锶铁氧体复合磁体磁性能的影响[J].材料科学与工艺,2015,23(5):94-98.DOI:10.11951/j.issn.1005-0299.20150517. |
| ZHONG Xichun,HU Geng,GUO Xingjia,LIU Zhongwu.Effect of binder on magnetic properties of bonded NdFeB/Sr-ferrite hybrid magnets[J].Materials Science and Technology,2015,23(5):94-98.DOI:10.11951/j.issn.1005-0299.20150517. |
|
| 摘要: |
| 为获得磁性能适中的磁体,采用流动温压成型技术制备了各向同性粘结NdFeB/锶铁氧体复合磁体.利用振动样品磁强计(VSM)研究了不同粘结剂对粘结NdFeB/锶铁氧体复合磁体磁性能的影响.研究表明:环氧值适中的酚醛环氧树脂制备的磁体具有较好的磁性能；当采用环氧值为0.480 mol/100 g酚醛环氧树脂BPANE8200H做粘结剂时,粘结NdFeB/锶铁氧体复合磁体获得了最佳的磁性能:Br=0.55 T,Hcj=620.6 kA/m, (BH)max=45.6 kJ/m3.在保证磁体磁性能的前提下兼顾力学性能,粘结磁体流动温压成型温度参数的设置必须考虑粘结剂的软化点温度. |
| 关键词: 粘结复合磁体 粘结剂 流动温压成型 磁性能 软化点 |
| DOI：10.11951/j.issn.1005-0299.20150517 |
| 分类号:TM273 |
| 基金项目:广东省教育部产学研结合资助项目(2009B090300273)；稀土改性高性能铁氧体环保橡胶磁的研究及产业化项目(2010A090200042). |
|
| Effect of binder on magnetic properties of bonded NdFeB/Sr-ferrite hybrid magnets |
|
ZHONG Xichun, HU Geng, GUO Xingjia, LIU Zhongwu
|
|
(School of Materials Science and Engineering, South China University of Technology, Guangzhou 510640,China)
|
| Abstract: |
| In order to obtain moderate magnetic properties, isotropic bonded NdFeB/Sr-ferrite hybrid magnets were synthesized by using warm flow compaction (WFC) technique. The effects of different types of binders on the magnetic properties of the hybrid magnets had been investigated using a vibrating sample magnetometer (VSM). The results showed that the magnets prepared by epoxy resin of mezzo epoxy value exhibited better magnetic properties than the others. The optimum magnetic properties of Br=0.55 T, Hcj=620.6 kA/m, and (BH)max=45.6 kJ/m3 were obtained by using BPANE8200H epoxy phenolic resin with epoxy value of 0.480 mol/100 g as the binder. To ensure magnetic and mechanical properties of the bonded magnets, softening point temperature of the binder must be considered when setting the molding temperature parameter for warm flow compaction (WFC) processing. |
| Key words: bonded hybrid magnet binder WFC magnetic properties softening point |