| 引用本文: | 王海涛,王连峥,王子相.汽车继电器用AgMeO触点材料不同配对方式时的性能[J].材料科学与工艺,2019,27(4):17-23.DOI:10.11951/j.issn.1005-0299.20180252. |
| WANG Haitao,WANG Lianzheng,WANG Zixiang.Performance of AgMeO contact materials for automotive relays in different pairing modes[J].Materials Science and Technology,2019,27(4):17-23.DOI:10.11951/j.issn.1005-0299.20180252. |
|
| 本文已被：浏览 1031次 下载 1627次 |
码上扫一扫！ |
|
|
| 汽车继电器用AgMeO触点材料不同配对方式时的性能 |
|
王海涛1,2, 王连峥1,2,王子相1,2
|
|
(1.省部共建电工装备可靠性与智能化国家重点实验室(河北工业大学),天津 300130; 2.河北省电磁场与电器可靠性重点实验室(河北工业大学),天津 300130)
|
|
| 摘要: |
| 为了探究触点配对方式对汽车继电器电接触性能的影响，选取AgMeO型触头材料进行实验，采用粉末冶金法制备AgSnO2, AgCuO和AgZnO 3种触头材料，并测量其物理性能，采用JF04C电接触触点材料测试系统，按5种不同触点配对方式进行电接触实验，并对实验前后的阴阳极触点进行称量，实验结果表明：触点配对方式对接触电阻，材料转移和损耗影响较大，对燃弧能量的影响较小，通过对触点进行不对称配对可以明显降低接触电阻和材料转移和损耗，明显改善汽车继电器的接触性能. |
| 关键词: AgMeO触点材料 配对方式 粉末冶金法 接触电阻 燃弧能量 材料转移及损耗 |
| DOI：10.11951/j.issn.1005-0299.20180252 |
| 分类号:TM501 |
| 文献标识码:A |
| 基金项目:国家自然科学基金资助项目(51777057);河北省自然科学基金项目(E2016202106);河北省高等学校科学技术研究项目(ZD2016078). |
|
| Performance of AgMeO contact materials for automotive relays in different pairing modes |
|
WANG Haitao1,2,WANG Lianzheng1,2,WANG Zixiang1,2
|
|
(1.State Key Laboratory of Reliability and Intelligence of Electrical Equipment(Hebei University of Technology), Tianjin 300130, China; 2. Key Laboratory of Electromagnetic Field and Electrical Apparatus Reliability of Hebei Province(Hebei University of Technology), Tianjin 300130, China)
|
| Abstract: |
| In order to investigate the effect of contact pairing mode on the automotive relays electrical contact properties, AgMeO contact materials were selected for experiment.Three kinds of contact materials AgSnO2, AgCuO, and AgZnO were prepared by powder metallurgy method, and their physical properties were measured. The electric contact test was carried out according to five different contact pairing modes using JF04C electric contact materials testing system, then cathode and anode were weighed before and after the experiment. Experimental results show that the contact resistance, material transfer and loss were greatly affected by the contact pairing mode, but the effect on the arc energy was small.Contact resistance, material transfer and loss could be significantly reduced by asymmetric contact pairing, and contact performance of automotive relays could be significantly improved. |
| Key words: AgMeO contact materials pairing mode powder metallurgy method contact resistance arc energy material transfer and loss |