| 引用本文: | 杨一群,李和汀,孙亚东,周芸,左孝青,桓源峰,刘沁曦.粉末增塑挤压制备Al2O3/430L复合型蜂窝材料的组织与性能[J].材料科学与工艺,2017,25(3):19-25.DOI:10.11951/j.issn.1005-0299.20160389. |
| YANG Yiqun,LI Heting,SUN Yadong,ZHOU Yun,ZUO Xiaoqing,HUAN Yuanfeng,LIU Qinxi.Structure and properties of Al2O3/430L composite honeycombs fabricated by plasticizing powder extrusion[J].Materials Science and Technology,2017,25(3):19-25.DOI:10.11951/j.issn.1005-0299.20160389. |
|
| 本文已被：浏览 2004次 下载 1321次 |
码上扫一扫！ |
|
|
| 粉末增塑挤压制备Al2O3/430L复合型蜂窝材料的组织与性能 |
|
杨一群1,李和汀1,孙亚东1,周芸1,左孝青1,桓源峰2,刘沁曦2
|
|
(1.昆明理工大学 材料科学与工程学院,昆明 650093; 2.昆明贵金属研究所,昆明 650106)
|
|
| 摘要: |
| 为制备性能优良的Al2O3/430L复合型蜂窝载体材料，本文以430L不锈钢合金粉末、Al2O3粉末、粘结剂为原料，采用粉末增塑挤压技术挤压成形，并在1 100 ℃真空中烧结2 h获得Al2O3/430L复合型蜂窝材料.借助SEM、XRD及万能试验机, 研究了添加Al2O3对Al2O3/430L复合型蜂窝材料的组织与性能的影响.研究表明：金属粉末颗粒在烧结过程中结合形成的基体组织为α-Fe(Cr)，在基体晶粒间孔隙处和表面弥散分布着Al2O3颗粒.添加少量的Al2O3可提高烧结密度，制件表面光滑.随着Al2O3添加量增加，蜂窝材料表面负载催化涂层的能力增强；抗压强度随Al2O3添加量的增加先升高后降低，在Al2O3含量为2.5wt.%时，最大抗压强度达27 MPa.添加2.5wt.%Al2O3所制备的Al2O3/430L复合型蜂窝材料力学性能最佳、表面负载催化涂层的能力优良.
|
| 关键词: Al2O3/430L 金属蜂窝 粉末增塑挤压 载体材料 430L不锈钢 |
| DOI：10.11951/j.issn.1005-0299.20160389 |
| 分类号:TB331 |
| 文献标识码:A |
| 基金项目:国家自然科学基金资助项目(51264024). |
|
| Structure and properties of Al2O3/430L composite honeycombs fabricated by plasticizing powder extrusion |
|
YANG Yiqun1,LI Heting1,SUN Yadong1,ZHOU Yun1,ZUO Xiaoqing1,HUAN Yuanfeng2,LIU Qinxi2
|
|
(1.Faculty of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093, China; 2.Kunming Institute of Precious Metals,Kunming 650106, China)
|
| Abstract: |
| To fabricate Al2O3 /430L composite honeycombs with high-performance, with pure 430L powder, Al2O3 and a binder as raw materials, Al2O3 /430L composite honeycombs were fabricated by plasticizing powder extrusion and sintering at 1 100 ℃ for 2 h under vacuum conditions. The effect of adding Al2O3 on the microstructure and properties of Al2O3 /430L composite honeycombs has been investigated by SEM, XRD and universal testing machine.The results show that, by sintering at 1 100 ℃ for 2 h in a vacuum, metal powder particles were jioned together to form α-Fe matrix, and Al2O3 is distributed on the surface and pore of matrix. Adding a small amount of Al2O3 can improve the density of sintered part, and make the part surface smooth. Increasing the amount of Al2O3can improve the surface bonding strength of honeycomb carriers with catalytic coating. Compressive strength of the part increases at first and then decreases with the increase of the content of Al2O3, and the peak value reaches at 2.5wt.% Al2O3 and maximum compressive strength 27 MPa.The Al2O3 /430L composite honeycombs with 2.5wt.% Al2O3 have best mechanical properties and high surface coating adhesion.
|
| Key words: Al2O3/430L metallic honeycomb plasticizing powder extrusion carrier material 430L stainless steel |