| 引用本文: | 李东辉,王英,郑文忠.碱激发矿渣陶粒混凝土砌块高温后力学性能[J].哈尔滨工业大学学报,2019,51(6):46.DOI:10.11918/j.issn.0367-6234.201808142 |
| LI Donghui,WANG Ying,ZHENG Wenzhong.Mechanical properties of alkali-activated slag ceramsite concrete block after exposure to high temperature[J].Journal of Harbin Institute of Technology,2019,51(6):46.DOI:10.11918/j.issn.0367-6234.201808142 |
|
| 本文已被：浏览 1380次 下载 1078次 |
码上扫一扫！ |
|
|
| 碱激发矿渣陶粒混凝土砌块高温后力学性能 |
|
李东辉1,2,3,王英1,2,3,郑文忠1,2,3
|
|
(1.哈尔滨工业大学 土木工程学院,哈尔滨150090; 2.结构工程灾变与控制教育部重点实验室(哈尔滨工业大学),哈尔滨150090; 3.土木工程智能防灾减灾工业和信息化部重点实验室(哈尔滨工业大学),哈尔滨150090)
|
|
| 摘要: |
| 为研究碱激发矿渣陶粒混凝土砌块高温后力学性能,完成了MU10和MU20两个强度等级常温下及历经400、600、700、800、900、1 000、1 100 ℃高温后各24个碱激发矿渣陶粒混凝土砌块抗压试验.发现MU10和MU20砌块高温后抗压强度在20~1 100 ℃间随历经温度的升高而线性降低.基于试验结果,建立了高温后碱激发矿渣陶粒混凝土砌块抗压强度随历经温度而变化的计算公式. |
| 关键词: 碱激发矿渣陶粒混凝土 砌块 历经温度 高温后 抗压强度 |
| DOI：10.11918/j.issn.0367-6234.201808142 |
| 分类号:TU377 |
| 文献标识码:A |
| 基金项目:国家自然科学基金(51478142) |
|
| Mechanical properties of alkali-activated slag ceramsite concrete block after exposure to high temperature |
|
LI Donghui1,2,3,WANG Ying1,2,3,ZHENG Wenzhong1,2,3
|
|
(1.School of Civil Engineering, Harbin Institute of Technology, Harbin 150090, China; 2.Key Lab of Structures Dynamic Behavior and Control (Harbin Institute of Technology), Ministry of Education, Harbin 150090, China; 3.Key Lab of Smart Prevention and Mitigation of Civil Engineering Disasters (Harbin Institute of Technology), Ministry of Industry and Information Technology, Harbin 150090, China)
|
| Abstract: |
| To investigate the mechanical properties of alkali-activated slag ceramsite concrete blocks after exposure to high temperature, compression tests were conducted on 48 alkali-activated slag ceramsite concrete blocks with two strength grades, MU10 and MU20, and all the specimens were exposed to normal temperature and a temperature history of 400 ℃, 600 ℃, 700 ℃, 800 ℃, 900 ℃, 1 000 ℃, and 1 100 ℃. The results show that the compressive strengths of MU10 and MU20 ceramsite concrete blocks exhibited a linear decrease with the increase of the heating temperature from 20 ℃ to 1 100 ℃. Based on the test results, the formulas were constructed to calculate the compressive strengths of the alkali-activated slag ceramsite concrete blocks after exposure to high temperature in term of the heating temperatures. |
| Key words: alkali-activated slag ceramsite concrete block heating temperatures exposure to high temperature compressive strength |